Best welding tips: how to become a more skilled welder and how to pick the best welding equipment. If a ball forms on the end of your rod when welding you are doing something wrong. It is usually one or more of these things: Too long an arc… • Too much torch angle • Not enough amperage for the rod size • Bad filler rod angle • Or some combination of all of these things. The 2 things I see most often with noobs are too long an arc AND too much torch angle. A long arc sets TIG welding back a few decades because it’s more like gas welding with an oxyfuel torch. The heat is not concentrated and you get this big heated arc plume like you get with a gas welding torch. Why would you want that? Your arc length should not be much more than the diameter of your tungsten electrode. I know that’s pretty close and if you get too close you will be grinding electrodes more than you are welding. But if you want really good welds, you need to use a tight arc.
Not all aluminum alloys are weldable: For example: 7075 and 2024 are not considered readily weldable using TIG welding. You can usually TIG weld them and they might be fine for a tool tote or some little art project…but don’t be fooled. You can’t depend on the welds in critical applications. Take a tree stand for instance. Lets say Joe gets a good deal on some aluminum angle iron at his friends scrap yard and he decides to make a tree stand. Joe has no way of knowing what alloy of aluminum he got from the scrap yard. He makes the tree stand, it holds together and looks just fine. The welds are real pretty…like a stack of dimes. One day he is sitting in his tree stand about 20 feet up a tree. The stress corrosion that has been happening on a microstrucutural level since he finished welding the tree stand finally comes home to roost and CRACK!!
Do a practice run. This may sound silly, but you’ll find that many professional welders do this before every pass. Get in the most comfortable position you can, with support blocks in place if helpful, and run your hands along the path they will traverse as you make the weld. You will often find that a slight adjustment of your position will allow you to make a longer pass, or to move your hands with less stress. Any strain in your position will have a negative impact on the weld. Also, you build valuable muscle memory when making your practice run, which will help keep everything on track when you make the ‘real’ pass. Clean a contaminated electrode immediately! Every welder will contaminate their electrode at some point, but it’s essential that you replace a contaminated electrode immediately. I usually keep a group of pre-sharpened electrodes right on my welding bench, so I can swap them out without having to walk to my grinder.
Searching for the best Welding Equipment? We recommend Welding Supplies Direct & Associate company TWS Direct Ltd is an online distributor of a wide range of welding supplies, welding equipment and welding machines. We supply Plasma Cutters, MIG, TIG, ARC Welding Machines and support consumables to the UK, Ireland and Europe.
Before you start welding, make sure all of your connections are tight — from the front of the MIG gun to the power pin attaching it to the power source. Also be certain there is no spatter buildup on your consumables and that you have a ground cable as close to the workspace as possible. Whenever possible, hook the ground cable on the weldment. If that is not possible, hook it to a bench. But remember: The closer it is to the arc, the better. If you have a questionable ground, it can cause the gun to overheat, impacting contact tip life and weld quality. In addition, regularly clean any shavings from the welding wire or debris that collects on your consumable parts and in your liner using clean compressed air.